Oxygen adsorption induced superconductivity in ultrathin FeTe film on SrTiO3(001)
arXiv:2110.06417 · doi:10.3390/ma14164584
Abstract
The phenomenon of oxygen incorporation induced superconductivity in iron telluride (Fe1+yTe, with antiferromagnetic (AFM) orders) is intriguing and quite different from the case of FeSe. Until now, the microscopic origin of the induced superconductivity and the role of oxygen are far from clear. Here, by combining in-situ scanning tunneling microscopy/spectroscopy (STM/STS) and x-ray photoemission spectroscopy (XPS) on oxygenated FeTe, we found physically adsorbed O2 molecules crystallized into c(2/3x2) structure as an oxygen overlayer at low temperature, which was vital for superconductivity. The O2 overlayer were not epitaxial on the FeTe lattice, which implied weak O2-FeTe interaction but strong molecular interactions. Energy shift observed in the STS and XPS measurements indicated hole doping effect from the O2 overlayer to the FeTe layer, leading to a superconducting gap of 4.5 meV opened across the Fermi level. Our direct microscopic probe clarified the role of oxygen on FeTe and emphasized the importance of charge transfer effect to induce superconductivity in iron-chalcogenide thin films.
15 pages,4 figures
References in corpus (5)
- Dynamics and mechanism of oxygen annealing in FeTeSe single crystal
- Evolution of superconductivity by oxygen annealing in FeTe0.8S0.2
- Observation of robust edge superconductivity in Fe(Se,Te) under strong magnetic perturbation
- Observation of two-level critical state in the superconducting FeTe thin films
- Size Dependence of Oxygen-annealing Effects on Superconductivity of Fe{1+y}Te{1-x}S{x}