The maximum recoverable strain of most crystalline solids is less than 1% because plastic deformation or fracture usually occurs at a small strain. In this work, we show that a SrNi $_{2}$ P $_{2}$ micropillar exhibits pseudoelasticity with a large maximum recoverable strain of ~14% under uniaxial compression via unique reversible structural transformation, double lattice collapse-expansion that is repeatable under cyclic loading. Its high yield strength (~3.8 $\pm$ 0.5 GPa) and large maximum recoverable strain bring out the ultrahigh modulus of resilience (~146 $\pm$ 19MJ/m $^{3}$ ) a few orders of magnitude higher than that of most engineering materials. The double lattice collapse-expansion mechanism shows stress-strain behaviors similar with that of conventional shape memory alloys, such as hysteresis and thermo-mechanical actuation, even though the structural changes involved are completely different. Our work suggests that the discovery of a new class of high performance ThCr $_{2}$ Si $_{2}$ -structured materials will open new research opportunities in the field of pseudoelasticity.

Pseudoelasticity of SrNi2​P2​ micropillar via Double Lattice Collapse and Expansion