Fluorine solubility and superconducting properties of Sm(O,F)BiS${}_2$ single crystals

Abstract

Sm(O,F)BiS2 superconducting single crystals with various nominal F contents have been grown using KI-KCl flux. The solid solution limit of F at the O-site in Sm(O,F)BiS2 single crystals was approximately less than 20 at%. F concentrations of Sm(O,F)BiS2 single crystals were hardly controlled by nominal F contents. It suggests the existence of intrinsic stable phase. Superconductivity was shown at around 5 K. Superconducting transition temperature with zero resistivity were increased with increasing nominal F contents within less than 70 at% in O-site, despite similar F concentration and c-axis lattice constants.

References in corpus (7)

• Superconductivity at 43 K in Samarium-arsenide Oxides $SmFeAs{O}_{1-x}{F}_x$
• Superconductivity in novel BiS2-based layered superconductor LaO1-xFxBiS2
• Superconductivity Appears in the Vicinity of an Insulating-Like Behavior in CeO${}_{1-x}$F${}_x$BiS${}_2$
• In-plane chemical pressure essential for superconductivity in BiCh2-based (Ch: S, Se) layered structure
• Superconductivity at 6 K and the violation of Pauli limit in Ta2PdxS5
• Synthesis and properties of SmO0.5F0.5BiS2 and enhancement in Tc in La1-ySmyO0.5F0.5BiS2
• Growth of superconducting Sm(O,F)BiS2 single crystals

Cited by in corpus (1)

• Suppression of superconductivity by Sb-substitution into CeOBiS2 single crystals