Systematic electrochemical etching of various metal tips for tunneling spectroscopy and scanning probe microscopy

Abstract

Hard point-contact spectroscopy and scanning probe microscopy/spectroscopy are powerful techniques for investigating materials with strong expandability. To support these studies, tips with various physical and chemical properties are required. To ensure the reproducibility of experimental results, the fabrication of tips should be standardized, and a controllable and convenient system should be set up. Here a systematic methodology to fabricate various tips is proposed, involving electrochemical etching reactions. The reaction parameters fall into four categories: solution, power supply, immersion depth, and interruption. An etching system was designed and built so that these parameters could be accurately controlled. With this system, etching parameters for copper, silver, gold, platinum/iridium alloy, tungsten, lead, niobium, iron, nickel, cobalt, and permalloy were explored and standardized. Among these tips, silver and niobium's new recipes were explored and standardized. Optical and scanning electron microscopies were performed to characterize the sharp needles. Relevant point-contact experiments were carried out with an etched silver tip to confirm the suitability of the fabricated tips.

arXiv commentThe article has been accepted by Review of Scientific Instruments. After it is published, it will be found at https://aip.scitation.org/journal/rsi

References in corpus (12)

• Advances in atomic force microscopy
• Observation of Majorana fermions with spin selective Andreev reflection in the vortex of topological superconductor
• Observation of superconductivity in 3D Dirac semimetal Cd3As2 crystal
• Unconventional Superconductivity at Mesoscopic Point-contacts on the 3-Dimensional Dirac Semi-metal Cd${}_3$As${}_2$
• Tip induced unconventional superconductivity on Weyl semimetal TaAs
• Mesoscopic superconductivity and high spin polarization coexisting at metallic point contacts on the Weyl semimetal TaAs
• Evidence for two-gap nodeless superconductivity in SmFeAsO${}_{0.8}$F${}_{0.2}$ from point-contact Andreev-reflection spectroscopy
• Superconductivity in topologically nontrivial material Au2Pb
• The energy gap of intermediate-valent SmB6 studied by point-contact spectroscopy
• Andreev Reflection Spectroscopy in Niobium Point Contacts in Magnetic Field
• Enhanced superconductivity at the interface of W/Sr${}_2$RuO${}_4$ point contact
• Automated fabrication technique of gold tips for use in point-contact spectroscopy