Stable ordered phases of cuprous iodide with complexes of copper vacancies

Abstract

We perform an exhaustive theoretical study of the phase diagram of Cu-I binaries, focusing on Cu-poor compositions, relevant for p-type transparent conduction. We find that the interaction between neighboring Cu vacancies is the determining factor that stabilizes non-stoichiometric zincblende phases. This interaction leads to defect complexes where Cu vacancies align preferentially along the [100] crystallographic direction. It turns out that these defect complexes have an important influence on hole conductivity, as they lead to dispersive conducting $p$-states that extend up to around 0.8 eV above the Fermi level. We furthermore observe a characteristic peak in the density of electronic states, which could provide an experimental signature for this type of defect complexes.

References in corpus (4)

• Multicomponent multisublattice alloys, nonconfigurational entropy and other additions to the Alloy Theoretic Automated Toolkit
• Crystal structure prediction using the Minima Hopping method
• Rungs 1 to 4 of DFT Jacob's ladder: extensive test on the lattice constant, bulk modulus, and cohesive energy of solids
• Performance of the strongly constrained and appropriately normed density functional for solid-state materials