Magnetic properties of $(F{e}_{1-x}M{n}_x{)}_{2}Al{B}_2$ and the impact of substitution on the magnetocaloric effect

Abstract

In this work, we investigate the magnetic structures of $(F{e}_{1-x}M{n}_x{)}_{2}Al{B}_2$ solid-solution quaternaries in the $x=0$ to $1$ range using x-ray and neutron diffraction, magnetization measurements, and mean-field theory calculations. While $F{e}_{2}Al{B}_2$ and $M{n}_{2}Al{B}_2$ are known to be ferromagnetic (FM) and antiferromagnetic (AFM), respectively, herein we focused on the magnetic structure of their solid solutions, which is not well understood. The FM ground state of $F{e}_{2}Al{B}_2$ becomes a canted AFM at $x\approx 0.2$, with a monotonically diminishing FM component until $x\approx 0.5$. The FM transition temperature ($T_C$) decreases linearly with increasing $x$. These changes in magnetic moments and structures are reflected in anomalous expansions of the lattice parameters, indicating a magnetoelastic coupling. Lastly, the magnetocaloric properties of the solid solutions were explored. For $x=0.2$ the isothermal entropy change is smaller by 30% than it is for $F{e}_{2}Al{B}_2$, while the relative cooling power is larger by 6%, due to broadening of the temperature range of the transition.

arXiv commentFinal version as published in physical review materials

References in corpus (4)

• Inverse magnetocaloric effect in ferromagnetic Ni-Mn-Sn alloys
• Electronic structure and magnetic properties in $T_2{\text{AlB}}_2$ ($T$ = Fe, Mn, Cr, Co, and Ni) and their alloys
• Magnetic and mechanical effects of Mn substitutions in AlFe2B2
• Near room temperature antiferromagnetic ordering with a potential low dimensional magnetism in AlMn${}_2$B${}_2$

Cited by in corpus (1)

• Reactive single-step hot-pressing and magnetocaloric performance of polycrystalline Fe${}_2$Al${}_{1.15-x}$B${}_2$Ge${}_x$Ga${}_x$ ($x=0,0.05$) MAB phases