Dewetted Au nanoparticles on TiO${}_2$ surfaces -- Evidence of a size-independent plasmonic photo-electrochemical response

Abstract

Flat TiO${}_2$ layers are deposited by magnetron sputtering on Ti/Si wafers. The TiO${}_2$ surfaces are then sputter-coated with thin Au films of a nominal thickness of 0.5-10 nm that are converted by solid-state dewetting into Au nanoparticles of tuneable size and spacing; the Au nanoparticle size can be tuned over a broad range, i.e. ca. 3-200 nm. The Au-decorated TiO${}_2$ surfaces enable plasmonic photo-electrochemical water splitting under visible light illumination (450-750 nm). The water splitting performance reaches a maximum for TiO${}_2$ layers decorated with ~ 30 nm-sized Au particles. As expected, optical absorption measurements show a red shift of the plasmonic extinction band with increasing the Au nanoparticle size. However, the plasmonic photocurrent is found to peak at ~ 600 nm regardless of the size of the Au nanoparticles, i.e. the plasmonic photocurrent band position is size-independent. Such a remarkable observation can be ascribed to a hot electron injection cut-off effect.

References in corpus (6)

• How to face the loss in plasmonics and metamaterials
• Materials Pushing the Application Limits of Wire Grid Polarizers further into the Deep Ultraviolet Spectral Range
• Efficient Photocatalytic H2 Evolution: Controlled Dewetting-Dealloying to Fabricate Site-Selective High-activity Nanoporous Au Particles on Highly Ordered TiO2 Nanotube Arrays
• Noble metals on anodic TiO2 nanotubes mouths: Thermal dewetting of minimal Pt co-catalyst loading leads to significantly enhanced photocatalytic H2 generation
• Templated Dewetting-Alloying of NiCu Bilayers on TiO${}_2$ Nanotubes Enables Efficient Noble Metal-Free Photocatalytic $H_2$ Evolution
• Photocatalytic reduction and scavenging of Hg(II) over templated-dewetted Au on TiO${}_2$ nanotubes