Enhanced upper critical field in Co-doped Ba122 superconductors by lattice defect tuning
arXiv:1911.01080 · doi:10.1063/1.5098057
Abstract
Nanoscale defects in superconductors play a dominant role in enhancing superconducting properties through electron scattering, modulation of coherence length, and correlation with quantized magnetic flux. For iron-based superconductors (IBSCs) that are expected to be employed in high-field magnetic applications, a fundamental question is whether such defects develop an upper critical field (Hc2) similar to that of conventional BCS-type superconductors. Herein, we report the first demonstration of a significantly improved Hc2 in a 122-phase IBSC by introducing defects through high-energy milling. Co-doped Ba122 polycrystalline bulk samples (Ba(Fe,Co)2As2) were prepared by sintering powder which was partially mechanically alloyed through high-energy milling. A remarkable increase in full-width at half maximum of X-ray powder diffraction peaks, anomalous shrinkage in the a-axis, and elongation in the c-axis were observed. When lattice defects are introduced into the grains, semiconductor behavior of the electric resistivity at low temperature (T < 100 K), slight decrease in transition temperature (Tc), upturn of Hc2(T) near Tc, and a large increase in Hc2(T) slope were observed. The slope of Hc2(T) increased approximately by 50%, i.e., from 4 to 6 T/K, and exceeded that of single crystals and thin films. Defect engineering through high-energy milling is expected to facilitate new methods for the designing and tuning of Hc2 in 122-phase IBSCs.
14 pages, 5 figures, to be published in APL Materials
References in corpus (13)
- Superconductivity at 22 K in Co-doped BaFe2As2 Crystals
- Effects of Co substitution on thermodynamic and transport properties and anisotropic in Ba(FeCo)As single crystals
- Nearly Isotropic superconductivity in (Ba,K)Fe2As2
- Small anisotropy, weak thermal fluctuations, and high field superconductivity in Co-doped iron pnictide Ba(Fe1-xCox)2As2
- Advantageous grain boundaries in iron pnictide superconductors
- High intergrain critical current density in fine-grain (Ba0.6K0.4)Fe2As2 wires and bulks
- Upper critical field, anisotropy, and superconducting properties of BaKFeAs single crystals
- Strong Tc dependence for strained, epitaxial Ba(Fe1-xCox)2As2 thin films
- High transport current superconductivity in powder-in-tube Ba0.6K0.4Fe2As2 tapes at 27 tesla
- Possible superconductivity above 25 K in single crystalline Co-doped BaFeAs
- Doping-dependent critical current properties in K, Co, and P-doped BaFe2As2 single crystals
- Versatile fluoride substrates for Fe-based superconducting thin films
- Upper critical field anisotropy in BaFe2-xCoxAs2 single crystals synthesized without flux