Shape anisotropy of magnetic nanoparticles in (Co${}_{86}$Nb${}_{12}$Ta${}_2$)${}_x$(SiO${}_2$)${}_{1-x}$ composite films revealed by grazing-incidence small-angle X-ray scattering

Abstract

Structure of amorphous nangranular composite (Co${}_{86}$Nb${}_{12}$Ta${}_2$)${}_x$(SiO${}_2$)${}_{1-x}$ films was studied by means of grazing-incidence small-angle X-ray scattering as a function of atomic concentration $x$ of the metal fraction in vicinity of the percolation threshold. It has been established that the average size of magnetic nanoparticles increases with $x$ and this increment exhibit the anisotropic character. It was found that in a whole concentration range the particles are elongated along the growth direction perpendicular to the film plane. For the lowest concentration $x=0.193$ clusters with isotropic shape and average radius of 1 nm were observed, while for higher concentrations up to $x=0.665$ the average cluster length along the film normal is $1.5-7$ nm and the cross-section is $1-2$ nm.

References in corpus (1)

• All-optical control of ferromagnetic thin films and nanostructures