Three-dimensional in situ characterization of phase transformation induced austenite grain refinement in nickel-titanium

Abstract

Near-field and far-field high-energy diffraction microscopy and microcomputed tomography X-ray techniques were used to study a bulk single crystal nickel-titanium shape memory alloy sample subjected to thermal cycling under a constant applied load. Three-dimensional in situ reconstructions of the austenite microstructure are presented, including the structure and distribution of emergent grain boundaries. After one cycle, the subgrain structure is significantly refined, and heterogeneous Σ3 and Σ9 grain boundaries emerge. The low volume and uneven dispersion of the emergent Σ boundaries across the volume show why previous transmission electron microscopy investigations of Σ grain boundary formation were inconsistent.