Chemical stability and superconductivity in Ag-sheathed CaKFe4As4 superconducting tapes

Abstract

Ag-sheathed CaKFe4As4 superconducting tapes have been fabricated via the ex-situ powder-in-tube method. Thermal and X-ray diffraction analyses suggest that the CaKFe4As4 phase is unstable at high temperatures. It decomposes into the CaAgAs phase which reacts strongly with the silver sheath. We therefore sintered the tape at 500C and obtain a transport critical current density Jc(4.2 K, 0 T)~ 2.7x10^4 A/cm2. The pinning potential derived from magnetoresistance measurements is one order of magnitude lower than that of the (Ba/Sr)1-xKxFe2As2 tapes. Combining with the scanning electron microscopy and magneto-optical imaging results, we suggest that bad connectivity between superconducting grains caused by the low sintering temperature is the main factor responsible for the low Jc. However, this system is still a promising candidate for superconducting wires and tapes if we further optimize the post-annealing process to achieve better grain connectivity.

arXiv comment17 pages, 6 figures

References in corpus (16)

• Recent advances in iron-based superconductors toward applications
• High intergrain critical current density in fine-grain (Ba0.6K0.4)Fe2As2 wires and bulks
• Very strong intrinsic supercurrent carrying ability and vortex avalanches in (Ba,K)Fe2As2 superconducting single crystals
• Anisotropic thermodynamic and transport properties of single crystalline CaKFe${}_4$As${}_4$
• Realization of practical level current densities in Sr0.6K0.4Fe2As2 tape conductors for high-field applications
• To use or not to use cool superconductors?
• Ultra-high critical current densities, the vortex phase diagram and the effect of granularity of the stoichiometric high-Tc superconductor, CaKFe${}_4$As${}_4$
• Optimization of the Crystal Growth of the Superconductor CaKFe${}_4$As${}_4$ from Solution in the FeAs-CaFe${}_2$As${}_2$-KFe${}_2$As${}_2$ System
• Hot pressing to enhance the transport Jc of Sr0.6K0.4Fe2As2 superconducting tapes
• Fabrication and Transport Properties of 100 m Class Sr0.6K0.4Fe2As2 Wires and Pancake Coils
• Nodeless multiband superconductivity in stoichiometric single crystalline CaKFe${}_4$As${}_4$
• Enhancement of critical current densities in (Ba,K)Fe2As2 wires and tapes using HIP technique
• Direct observation of local K variation and its correlation to electronic inhomogeneity in (Ba1-xKx)Fe2As2 Pnictide
• Upper critical field of high quality single crystals of KFe${}_2$As${}_2$
• Upper critical field of isoelectron substituted SrFe${}_2$(As${}_{1-x}$P${}_x$)${}_2$
• Vortex pinning and dynamics in high performance Sr0.6K0.4Fe2As2 superconductor