High-pressure polymorphism of BaFe2Se3

Abstract

BaFe2Se3 is a potential superconductor material exhibiting transition at 11 K and ambient pressure. Here we extended the structural and performed electrical resistivity measurements on this compound up to 51 GPa and 20 GPa, respectively, in order to distinguish if the superconductivity in this sample is intrinsic to the BaFe2Se3 phase or if it is originating from minor FeSe impurities that show a similar superconductive transition temperature. The electrical resistance measurements as a function of pressure show that at 5 GPa the superconducting transition is observed at around 10 K, similar to the one previously observed for this sample at ambient pressure. This indicates that the superconductivity in this sample is intrinsic to the BaFe2Se3 phase and not to FeSe with Tc > 20 K at these pressures. Further increase in pressure suppressed the superconductive signal and the sample remained in an insulating state up to the maximum achieved pressure of 20 GPa. Single-crystal and powder X-ray diffraction measurements revealed two structural transformations in BaFe2Se3: a second order transition above 3.5 GPa from Pnma (CsAg2I3-type structure) to Cmcm (CsCu2Cl3-type structure) and a first order transformation at 16.6 GPa. Here, γ-BaFe2Se3 transforms into δ-BaFe2Se3 (Cmcm, CsCu2Cl3-type average structure) via a first order phase transition mechanism. This transitions is characterized by a significant shortening of the b lattice parameter of γ-BaFe2Se3 (17%) and accompanied by an anisotropic expansion in the orthogonal ac plane at the transition point.

References in corpus (14)

• Superconductivity at 36 K in beta-Fe1.01Se with the compression of the interlayer separation under pressure
• Fermi surface nesting induced strong pairing in iron-based superconductors
• Dome-shaped magnetic order competing with high-temperature superconductivity at high pressures in FeSe
• Pressure-induced high-Tc superconducting phase in FeSe: correlation between anion height and Tc
• Synthesis, crystal structure and chemical stability of the superconductor FeSe_{1-x}
• Iron Displacements and Magnetoelastic Coupling in the Spin-Ladder Compound BaFe2Se3
• Block magnetism coupled with local distortion in the iron-based spin-ladder compound BaFe2Se3
• Anisotropy in BaFe2Se3 single crystals with double chains of FeSe tetrahedra
• Spin Glass and Semiconducting Behavior in 1D BaFe2-δSe3 Crystals
• Crystal Structure of BaFe2Se3 as a Function of Temperature and Pressure: Phase Transition Phenomena and High-Order Expansion of Landau Potential
• Direct observation of the influence of the FeAs4 tetrahedron on superconductivity and antiferromagnetic correlations in Sr2VO3FeAs
• Compressibility and pressure-induced disorder in superconducting phase-separated Cs0.72Fe1.57Se2
• Magnetism of BaFe2Se3 studied by Mössbauer spectroscopy
• Cube-shape diffuse scattering and the ground state of ${\mathrm{BaMg}}_{1/3}{\mathrm{Ta}}_{2/3}{\mathrm{O}}_3$

Cited by in corpus (4)

• Robust block magnetism in the spin ladder compound BaFe${}_2$Se${}_3$ under hydrostatic pressure
• Magnetic-order-driven metal-insulator transitions in the quasi-one-dimensional spin-ladder compounds BaFe${}_2$S${}_3$ and BaFe${}_2$Se${}_3$
• Structural, magnetic, and electronic evolution of the spin-ladder system BaFe${}_2$S${}_{3-x}$Se${}_x$ with isoelectronic substitution
• Pressure-induced superconductivity in iron-based spin-ladder compound BaFe2+δ(S1-Sex)3