Well-Ordered In Adatoms at the In${}_2$O${}_3$(111) Surface Created by Fe Deposition

Abstract

Metal deposition on oxide surfaces usually results in adatoms, clusters, or islands of the deposited material, where defects in the surface often act as nucleation centers. Here an alternate configuration is reported. After the vapor deposition of Fe on the In${}_2$O${}_3$(111) surface at room temperature, ordered adatoms are observed with scanning tunneling microscopy. These are identical to the In adatoms that form when the sample is reduced by heating in ultrahigh vacuum. Density functional theory (DFT) calculations confirm that Fe interchanges with In in the topmost layer, pushing the excess In atoms to the surface where they arrange as a well-ordered adatom array.

References in corpus (4)

• Quantum ESPRESSO: a modular and open-source software project for quantum simulations of materials
• Subsurface Cation Vacancy Stabilization of the Magnetite (001) Surface
• Bulk and surface characterization of In${}_2$O${}_3$(001) single crystals
• Pt${}_3$Zr(0001): A substrate for growing well-ordered ultrathin zirconia films by oxidation

Cited by in corpus (2)

• Direct assessment of the proton affinity of individual surface hydroxyls with non-contact atomic force microscopy
• Interfacial Magnetic Anisotropy of Iron-Adsorbed Ferroelectric Perovskites: First-Principles and Machine Learning Study