Strong Electron-Phonon Coupling Superconductivity Induced by a Low-lying Phonon in IrGe

Abstract

The physical properties of the previously reported superconductor IrGe and the Rh1-xIrxGe solid solution are investigated. IrGe has an exceptionally high superconducting transition temperature (Tc = 4.7 K) among the isostructural 1:1 late-metal germanides MGe (M = Rh, Pd, Ir and Pt). Specific-heat measurements reveal that IrGe has an anomalously low Debye temperature, originating from a low-lying phonon, compared to the other MGe phases. A large jump at Tc in the specific-heat data clearly indicates that IrGe is a strong coupling superconductor. In the Rh1-xIrxGe solid solution, a relationship between an anomalous change in lattice constants and the Debye temperature is observed. We conclude that the unusually high Tc for IrGe is likely due to strong electron-phonon coupling derived from the presence of a low-lying phonon.

5 pages, 4 figures, 1 table

References in corpus (1)

• Extremely strong-coupling superconductivity and anomalous lattice properties in the beta-pyrochlore oxide KOs2O6

Cited by in corpus (8)

• Superconducting Properties of BaBi${}_3$
• NbIr${}_2$B${}_2$ and TaIr${}_2$B${}_2$ -- new low symmetry noncentrosymmetric superconductors with strong spin orbit coupling
• Characterization of the Heavy Metal Pyrochlore Lattice Superconductor CaIr2
• Ir d-band Derived Superconductivity in the Lanthanum-Iridium System LaIr3
• Ir 5$d$-band Derived Superconductivity in LaIr${}_3$
• Strong-Coupling Superconductivity in BaPd2As2 Induced by Soft Phonons in the ThCr2Si2-type Polymorph
• Superconductivity in MgPtSi: An orthorhombic variant of MgB2
• Superconductivity of centrosymmetric and non-centrosymmetric phases in antiperovskite (Ca,Sr)Pd${}_3$P