Mechanism of magnetostructural transformation in multifunctional Mn${}_3$GaC

Abstract

Mn${}_3$GaC undergoes a ferromagnetic to antiferromagnetic, volume discontinuous cubic-cubic phase transition as a function of temperature, pressure and magnetic field. Through a series of temperature dependent x-ray absorption fine structure spectroscopy experiments at the Mn K and Ga K edge, it is shown that the first order magnetic transformation in Mn${}_3$GaC is entirely due to distortions in Mn sub-lattice and with a very little role for Mn-C interactions. The distortion in Mn sub-lattice results in long and short Mn-Mn bonds with the longer Mn-Mn bonds favoring ferromagnetic interactions and the shorter Mn-Mn bonds favoring antiferromagnetic interactions. At the first order transition, the shorter Mn-Mn bonds exhibit an abrupt decrease in their length resulting in an antiferromagnetic ground state and a strained lattice.

Accepted in J. Appl. Phys. Please contact authors for supplementary information

References in corpus (6)

• Order by disorder and spiral spin liquid in frustrated diamond lattice antiferromagnets
• Reversible room-temperature magnetocaloric effect with large temperature span in antiperovskite compounds Ga1-xCMn3+x (x=0, 0.06, 0.07, and 0.08)
• Effect of carbon content on magnetostructural properties of Mn${}_3$GaC
• Magnetic ordering in the frustrated J1-J2 Ising chain candidate BaNd2O4
• Effect of composition on magnetocaloric properties of Mn${}_3$Ga${}_{(1-x)}$Sn${}_x$C
• Phase separated magnetic ground state in Mn${}_3$Ga${}_{0.45}$Sn${}_{0.55}$C

Cited by in corpus (1)

• Absence of first order magnetic transition, a curious case of Mn3InC