On the nature of the (de)coupling of the magnetostructural transition in Er${}_5$Si${}_4$

Abstract

In this report, a successful thermodynamical model was employed to understand the structural transition in Er${}_5$Si${}_4$, able to explain the decoupling of the magnetic and structural transition. This was achieved by the DFT calculations which were used to determine the energy differences at 0 K, using a LSDA+U approximation. It was found that the M structure as the stable phase at low temperatures as verified experimentally with a $\Delta F_0=-$0.262 eV. Finally, it was achieved a variation of Seebeck coefficient ($\sim$ 6 $\mu$V) at the structural transition which allow to conclude that the electronic entropy variation is negligible in the transition.

17 pages, 3 figures, 1 table