Various arsenic network structures in 112-type Ca1-xLaxFe1-yPdyAs2 revealed by synchrotron x-ray diffraction experiments
arXiv:1703.04204 · doi:10.1021/acs.inorgchem.6b03115
Abstract
Two novel 112-type palladium doped iron arsenides were synthesized and identified using comprehensive studies involving synchrotron x-ray diffraction and x-ray absorption near edge structure (XANES) experiments. Whereas in-plane arsenic zigzag chains were found in 112-type superconducting iron arsenide, Ca1-xLaxFeAs2 with maximum Tc = 34 K, deformed arsenic network structures appeared in 112-type materials such as longitudinal arsenics zigzag chains in CaFe1-yPdyAs2 (y ~ 0.51) and arsenic square sheets constructed via hypervalent bonding in Ca1-xLaxFe1-yPdyAs2 (x ~ 0.31, y ~ 0.30). As K-edge XANES spectra clarified the similar oxidization states around FeAs4 tetrahedrons, expecting us the possible parents for high Tc 112-type iron arsenide superconductors.
arXiv comment9 pages, 5 figures
References in corpus (15)
- Superconductivity of bulk CaC6
- Superconductivity in Ca1-xLaxFeAs2: A Novel 112-Type Iron Pnictide with Arsenic Zigzag Bonds
- Electron doped Ca10(Pt3As8)(Fe2As2)5 and Ca10(Pt4As8)(Fe2As2)5 - High Tc superconductors with skutterudite intermediary layers
- Superconductivity at 22.3 K in SrFe2-xIrxAs2
- Discovery of New Layered Iron Arsenide Superconductor (Ca,Pr)FeAs2
- Superconductivity at 38 K in Iron-Based Compound with Platinum-Arsenide Layers Ca10(Pt4As8)(Fe2-xPtxAs2)5
- Superconductivity and phase diagrams in 4d- and 5d-metal-doped iron arsenides SrFe_{2-x}M_xAs_2 (M = Rh, Ir, Pd)
- Tailoring the Superconductivity and Antiferromagnetic Order in SrFe2-xRhxAs2
- Superconductivity induced by doping Pd in SrFe2-xPdxAs2
- Superconductivity up to 35 K in the iron-platinum arsenides (CaFe1-xPtxAs)10Pt4-yAs8 with layered structures
- Enhanced Superconductivity up to 43 K by P/Sb Doping of Ca1-xLaxFeAs2
- Iron-platinum-arsenide superconductors Ca10(PtnAs8)(Fe2-xPtxAs2)5
- Superconductivity in Ca10(Ir4As8)(Fe2As2)5 with Square-Planar Coordination of Iridium
- Superconductivity and Crystal Structure of the Palladium-Iron-Arsenides Ca10(Fe1-xPdxAs)10Pd3As8
- Synchrotron X-ray Diffraction Study of Structural Phase Transition in Ca10(Ir4As8)(Fe2-xIrxAs2)