Colossal enhancement of electrical conductivity in Y2Ir2O7 nanoparticles

Abstract

We present a comparative study of the magnetic and electrical properties of polycrystalline and nanocrystalline Y2Ir2O7, the latter prepared using a new chemical route. We find that reduction in particle size leads to enhanced ferromagnetism and orders of magnitude enhancement of electrical conductivity in the nanocrystalline sample. Based on x ray photoelectron spectroscopy and x ray absorption near edge structure spectroscopy results, the phenomenon is attributed to the increased fraction of pentavalent oxidation state of Iridium and the resulting increase in double exchange interaction along with the weakening of spin orbit coupling strength in the nanocrystalline sample compared to the bulk.

14 pages, 9 figures

References in corpus (7)

• Novel Jeff = 1/2 Mott State Induced by Relativistic Spin-Orbit Coupling in Sr2IrO4
• Magnetic orders and topological phases from f-d exchange in pyrochlore iridates
• Magnetic Order in the Pyrochlore Iridates A2Ir2O7 (A = Y, Yb)
• Enhanced weak ferromagnetism and conductivity in hole-doped pyrochlore iridate Y2Ir2O7
• Direct Evidence for the 'All-in/All-out' Magnetic Structure in the Pyrochlore Iridates from $\mu$SR
• Magnetic state of pyrochlore Cd2Os2O7 emerging from strong competition of ligand distortions and longer-range crystalline anisotropy
• Weak quasistatic magnetism in the frustrated Kondo lattice Pr_2Ir_2O_7

Cited by in corpus (2)

• Coexistence of high electrical conductivity and weak ferromagnetism in Cr doped Y${}_2$Ir${}_2$O${}_7$ pyrochlore iridate
• Suppression of long range magnetic ordering and electrical conduction in Y${}_{1.7}$Bi${}_{0.3}$Ir${}_2$O${}_7$ thin film