Structural origins of the boson peak in metals: From high-entropy alloys to metallic glasses

Abstract

The boson peak appears in all amorphous solids and is an excess of vibrational states at low frequencies compared to the phonon spectrum of the corresponding crystal. Until recently, the consensus was that it originated from "defects" in the glass. The nature of these defects is still under discussion, but the picture of regions with locally disturbed short-range order and/or decreased elastic constants has gained some traction. Recently, a different theory was proposed: The boson peak was attributed to the first van Hove singularity of crystal lattices which is only smeared out by the disorder. This new viewpoint assumes that the van Hove singularity is simply shifted by the decreased density of the amorphous state and is therefore not a glass-specific anomaly. In order to resolve this issue, we use computer models of a four-component alloy, alternatively with chemical disorder (high-entropy alloy), structural disorder, and reduced density. Comparison to a reference glass of the same composition reveals that the boson peak consists of additional vibrational modes which can be induced solely by structural disorder. While chemical disorder introduces fluctuations of the elastic constants, we find that those do not lead to sufficient local softening to induce these modes. A boson peak due to a reduction of density could be excluded for the present metallic system.

9 pages, 8 figures

References in corpus (2)

• Inhomogeneous elastic response of silica glass
• Low temperature heat capacity of severely deformed metallic glass

Cited by in corpus (5)

• Relaxation and vibrational properties in metal alloys and other disordered systems
• Atomic theory of viscoelastic response and memory effects in metallic glasses
• Entropic Stabilization and Descriptors of Structural Transformation in High Entropy Alloys
• Quantifying Disorder One Atom at a Time Using an Interpretable Graph Neural Network Paradigm
• Low temperature features in the heat capacity of unary metals and intermetallics for the example of bulk aluminum and Al${}_3$Sc