Microstructural topology effects on the onset of ductile failure in multi-phase materials - a systematic computational approach

Abstract

Multi-phase materials are key for modern engineering applications. They are generally characterized by a high strength and ductility. Many of these materials fail by ductile fracture of the, generally softer, matrix phase. In this work we systematically study the influence of the arrangement of the phases by correlating the microstructure of a two-phase material to the onset of ductile failure. A single topological feature is identified in which critical levels of damage are consistently indicated. It consists of a small region of the matrix phase with particles of the hard phase on both sides in a direction that depends on the applied deformation. Due to this configuration, a large tensile hydrostatic stress and plastic strain is observed inside the matrix, indicating high damage. This topological feature has, to some extent, been recognized before for certain multi-phase materials. This study however provides insight in the mechanics involved, including the influence of the loading conditions and the arrangement of the phases in the material surrounding the feature. Furthermore, a parameter study is performed to explore the influence of volume fraction and hardness of the inclusion phase. For the same macroscopic hardening response, the ductility is predicted to increase if the volume fraction of the hard phase increases while at the same time its hardness decreases.

Cited by in corpus (9)

• How collective asperity detachments nucleate slip at frictional interfaces
• Competing damage mechanisms in a two-phase microstructure: how microstructure and loading conditions determine the onset of fracture
• Microscopic plasticity and damage in two-phase steels: on the competing role of crystallography and phase contrast
• Fracture initiation in multi-phase materials: a statistical characterization of microstructural damage sites
• Microstructural modeling of ductile fracture initiation in multi-phase materials
• Fracture in multi-phase materials: why some microstructures are more critical than others
• Fracture initiation in multi-phase materials: a systematic three-dimensional approach using a FFT-based solver
• Systematic and objective identification of the microstructure around damage directly from images
• Topology and morphology influences on the onset of ductile failure in a two-phase microstructure