Phase boundary between Na-Si clathrates of structures I and II at high pressures and high temperatures

Abstract

Understanding the covalent clathrate formation is a crucial point for the design of new superhard materials with intrinsic coupling of superhardness and metallic conductivity. Silicon clathrates have the archetype structures that can serve an existant model compounds for superhard clathrate frameworks "Si-B", "Si-C", "B-C" and "C" with intercalated atoms (e.g. alkali metals or even halogenes) that can assure the metalic properties. Here we report the in situ and ex situ studies of high-pressure formation and stability of clathrates Na8Si46 (structure I) and Na24+xSi136 (structure II). Experiments have been performed using standard Paris-Edinburgh cells (opposite anvils) up to 6 GPa and 1500 K. We have established that chemical interactions in Na-Si system and transition between two structures of clathrates occur at temperatures below silicon melting. The strong sensitivity of crystallization products to the sodium concentration have been observed. A tentative diagram of clathrate transformations has been proposed. At least up to ~6 GPa, Na24+xSi136 (structure II) is stable at lower temperatures as compared to Na8Si46 (structure I).

References in corpus (4)

• Ionic high-pressure form of elemental boron
• Superhard Phases of Simple Substances and Binary Compounds of the B-C-N-O System: from Diamond to the Latest Results (a Review)
• Synthesis of rock-salt MeO-ZnO solid solutions (Me = Ni2+, Co2+, Fe2+, Mn2+) at high pressure and high temperature
• Thermoelastic Equation of State of Boron Suboxide B6O up to 6 GPa and 2700 K: Simplified Anderson-Grüneisen Model and Thermodynamic Consistency

Cited by in corpus (1)

• Thermoelastic equation of state and melting of Mg metal at high pressure and high temperature