Electronic and magnetic structure of epitaxial NiO/Fe${}_3$O${}_4$(001) heterostructures grown on MgO(001) and Nb-doped SrTiO${}_3$(001)

Abstract

We study the underlying chemical, electronic and magnetic properties of a number of magnetite based thin films. The main focus is placed onto NiO/Fe${}_3$O${}_4$(001) bilayers grown on MgO(001) and Nb-SrTiO${}_3$(001) substrates. We compare the results with those obtained on pure Fe${}_3$O${}_4$(001) thin films. It is found that the magnetite layers are oxidized and Fe${}^{3+}$ dominates at the surfaces due to maghemite ($\gamma$-Fe${}_2$O${}_3$) formation, which decreases with increasing magnetite layer thickness. From a layer thickness of around 20 nm on the cationic distribution is close to that of stoichiometric Fe${}_3$O${}_4$. At the interface between NiO and Fe${}_3$O${}_4$ we find the Ni to be in a divalent valence state, with unambiguous spectral features in the Ni 2p core level x-ray photoelectron spectra typical for NiO. The formation of a significant NiFe${}_2$O${}_4$ interlayer can be excluded by means of XMCD. Magneto optical Kerr effect measurements reveal significant higher coercive fields compared to magnetite thin films grown on MgO(001), and a 45${}^{\circ }$ rotated magnetic easy axis. We discuss the spin magnetic moments of the magnetite layers and find that the moment increases with increasing thin film thickness. At low thickness the NiO/Fe${}_3$O${}_4$ films grown on Nb-SrTiO${}_3$ exhibits a significantly decreased spin magnetic moments. A thickness of 20 nm or above leads to spin magnetic moments close to that of bulk magnetite.

References in corpus (10)

• Spintronics: Fundamentals and applications
• Half-metallic ferromagnets: From band structure to many-body effects
• Subsurface Cation Vacancy Stabilization of the Magnetite (001) Surface
• Vanishing Fe 3d orbital moments in single-crystalline magnetite
• Physical characteristics and cation distribution of NiFe2O4 thin films with high resistivity prepared by reactive co-sputtering
• Enhanced ferrimagnetism in auxetic NiFe2O4 in the crossover to the ultrathin film limit
• Room Temperature In-plane <100> Magnetic Easy Axis for Fe3O4/SrTiO3(001):Nb Grown by Infrared PLD
• Temperature-Dependence of Magnetically-Active Charge Excitations in Magnetite across the Verwey Transition
• Magnetic coupling in highly-ordered NiO/Fe3O4(110): Ultrasharp magnetic interfaces vs. long-range magnetoelastic interactions
• Structure and morphology of epitaxially grown Fe3O4/NiO bilayers on MgO(001)

Cited by in corpus (5)

• Free-sustaining Three-dimensional S235 Steel-based Porous Electrocatalyst for Highly Efficient and Durable Oxygen Evolution
• Cation- and lattice-site-selective magnetic depth profiles of ultrathin $\mathrm{F}{\mathrm{e}}_3{\mathrm{O}}_4$(001) films
• Time-resolved diffraction and photoelectron spectroscopy investigation of the reactive molecular beam epitaxy of $\mathrm{F}{\mathrm{e}}_3{\mathrm{O}}_4$ ultrathin films
• Impact of strain and morphology on magnetic properties of Fe${}_3$O${}_4$/NiO bilayers grown on Nb:SrTiO${}_3$(001) and MgO(001)
• Structural and magnetic investigation of the interfaces of $\mathrm{F}{\mathrm{e}}_3{\mathrm{O}}_4/MgO(001)$ with and without NiO interlayer