Evidence for Defect-induced Superconductivity up to 49 K in (Ca1-xRx)Fe2As2

Abstract

To explore the origin of the unusual non-bulk superconductivity with a Tc up to 49 K reported in the rare-earth-doped CaFe2As2 , the chemical composition, magnetization, specific heat, resistivity, and annealing effect are systematically investigated on nominal (Ca1-xRx)Fe2As2 single crystals with different x's and R = La, Ce, Pr, and Nd. All display a doping-independent Tc once superconductivity is induced, a doping-dependent low field superconducting volume fraction f, and a large magnetic anisotropy η in the superconducting state, suggesting a rather inhomogeneous superconducting state in an otherwise microscale-homogenous superconductor. The wavelength dispersive spectroscopy and specific heat show the presence of defects which are closely related to f, regardless of the R involved. The magnetism further reveals that the defects are mainly superparamagnetic clusters for R = Ce, Pr, and Nd with strong intercluster interactions, implying that defects are locally self-organized. Annealing at 500 °C, without varying the doping level x, suppresses f profoundly but not the Tc. The above observations provide evidence for the crucial role of defects in the occurrence of the unusually high Tc ~ 49 K in (Ca1-xRx)Fe2As2 and are consistent with the interface-enhanced superconductivity recently proposed.

arXiv comment16 pages, 15 figures

References in corpus (22)

• Superconductivity at 38 K in the iron arsenide (Ba1-xKx)Fe2As2
• Superconductivity up to 37 K in (A1-xSrx)Fe2As2 with A=K and Cs
• LiFeAs: An Intrinsic FeAs-based Superconductor with Tc = 18K
• Superconductivity up to 29 K in SrFe2As2 and BaFe2As2 at high pressures
• Pressure-induced volume-collapsed tetragonal phase of CaFe2As2 as seen via neutron scattering
• Phase Separation and Magnetic Order in K-doped Iron Selenide Superconductor
• The Absence of Superconductivity in Single Phase CaFe2As2 under Hydrostatic Pressure
• Structural collapse and superconductivity in rare earth-doped CaFe2As2
• On the Structure of Vacancy Ordered Superconducting Alkali Metal Iron Selenide
• The Unusual Superconducting State at 49 K in Electron-Doped CaFe2As2 at Ambient
• Magnetism Driven by Anion Vacancies in Superconducting $\alpha$--FeSe${}_{1-x}$
• Nanoscale layering of antiferromagnetic and superconducting phases in Rb2Fe4Se5
• Local inhomogeneity and filamentary superconductivity in Pr-doped CaFe${}_2$As${}_2$
• Synthesis and properties of La-doped CaFe2As2 single crystals with Tc = 42.7 K
• Spin reorientation in TlFe1.6Se2 with complete vacancy ordering
• Nanoscale Surface Element Identification and Dopant Homogeneity in the High-$T_c$ Superconductor Pr${}_x$Ca${}_{1-x}$Fe${}_2$As${}_2$
• Transport properties and anisotropy in rare earth doped CaFe2As2 single crystals with Tc above 40 K
• Why is the superconducting Tc so high in rare-earth-doped CaFe2As2?
• Separation of antiferromagnetism and high-temperature superconductivity in Ca${}_{1-x}$La${}_x$Fe${}_2$As${}_2$ under pressure
• Thermodynamic evidence for pressure-induced bulk superconductivity in the Fe-As pnictide superconductor CaFe2As2
• Effects of post-annealing and cobalt co-doping on superconducting properties of (Ca,Pr)Fe2As2 single crystals
• High Pressure Effects on the Superconductivity in Rare-Earth Doped CaFe2As2

Cited by in corpus (3)

• Gate-induced superconductivity in a monolayer topological insulator
• Pressure-induced high-temperature superconductivity retained at ambient
• The Search for Higher $T_c$ in Houston