Magnetic and Thermal Properties of SmRh${}_2$Zn${}_{20}$ Single Crystal

Abstract

The magnetization, magnetic susceptibility, and specific heat of the single crystalline sample SmRh${}_2$Zn${}_{20}$ were measured. The valence of Sm ions in SmRh${}_2$Zn${}_{20}$ was found to be trivalent. No evidence of valence fluctuations was detected. SmRh${}_2$Zn${}_{20}$ is an antiferromagnet with $T_{\mathrm{N}}=$ 2.46 K. The observed $C(T,H)$ curves showed that $T_{\mathrm{N}}$ splits into two in the external field $H$ along the [001] and [101]directions. On the other hand, $T_{\mathrm{N}}$ in $H$ along the [111] direction did not split, decreasing to 2.20 K at $H=7$ T. At 2 K, the magnetization $M_{111}$ in $H$ along the [111] direction increased linearly with increasing field, while $M_{001}$ and $M_{101}$ deviated upward slightly from the linear dependence. We analyzed the observed magnetic and thermal properties of SmRh${}_2$Zn${}_{20}$ taking into account the crystalline-electric-field effect, the Zeeman energy, and the exchange interaction. The theoretical calculation well reproduced the experimental $\chi (T)$, $M(H)$, $C(T,H)$ and $T_{\mathrm{N}}(H)$. The sublattice magnetic moments are expected to be along the $⟨111⟩$ direction below $T_{\mathrm{N}}$ at $H=0$ T. Variations of the magnetic structures induced by the external magnetic fields in a narrow temperature region around $T_{\mathrm{N}}$ are inferred on the basis of theoretical calculations.

14 pages, 8 figures