Large exchange bias in polycrystalline MnN/CoFe bilayers at room temperature

Abstract

We report on the new polycrystalline exchange bias system MnN/CoFe, which shows exchange bias of up to 1800Oe at room temperature with a coercive field around 600Oe. The room temperature values of the interfacial exchange energy and the effective uniaxial anisotropy are estimated to be $J_{\mathrm{eff}}=0.41\mathrm{mJ}/{\mathrm{m}}^2$ and $K_{\mathrm{eff}}=37\mathrm{kJ}/{\mathrm{m}}^3$. The thermal stability was found to be tunable by controlling the nitrogen content of the MnN. The maximum blocking temperature exceeds $325^{\circ }$C, however the median blocking temperature in the limit of thick MnN is $160^{\circ }$C. Good oxidation stability through self-passivation was observed, enabling the use of MnN in lithographically defined microstructures. As a proof-of-principle we demonstrate a simple GMR stack exchange biased with MnN, which shows clear separation between parallel and antiparallel magnetic states. These properties come along with a surprisingly simple manufacturing process for the MnN films.

7 pages, 6 figures

Cited by in corpus (10)

• Exchange interactions and Curie temperatures of the tetrametal nitrides Cr4N, Mn4N, Fe4N, Co4N, and Ni4N
• Giant perpendicular exchange bias with antiferromagnetic MnN
• Spin-orbit torque induced electrical switching of antiferromagnetic MnN
• Nitrogen-Based Magneto-Ionic Manipulation of Exchange Bias in CoFe/MnN Heterostructures
• Anisotropy in Antiferromagnets
• Correlation of tunnel magnetoresistance with the magnetic properties in perpendicular CoFeB-based junctions with exchange bias
• Thermal Contribution in the Electrical Switching Experiments with Heavy Metal / Antiferromagnet Structures
• Improved thermal stability in doped MnN/CoFe exchange bias systems
• Room temperature exchange bias in BiFeO3 / Co-Fe bilayers
• The Multi-Scale Dynamics of All-Optical Exchange Bias Reversal