Direct measurement of the magnetic anisotropy field in Mn--Ga and Mn--Co--Ga Heusler films

Abstract

The static and dynamic magnetic properties of tetragonally distorted Mn--Ga based alloys were investigated. Static properties are determined in magnetic fields up to 6.5~T using SQUID magnetometry. For the pure Mn${}_{1.6}$Ga film, the saturation magnetisation is 0.36~MA/m and the coercivity is 0.29~T. Partial substitution of Mn by Co results in Mn${}_{2.6}$Co${}_{0.3}$Ga${}_{1.1}$. The saturation magnetisation of those films drops to 0.2~MA/m and the coercivity is increased to 1~T. Time-resolved magneto-optical Kerr effect (TR-MOKE) is used to probe the high-frequency dynamics of Mn--Ga. The ferromagnetic resonance frequency extrapolated to zero-field is found to be 125~GHz with a Gilbert damping, $\alpha$, of 0.019. The anisotropy field is determined from both SQUID and TR-MOKE to be 4.5~T, corresponding to an effective anisotropy density of 0.81~MJ/m${}^3$. Given the large anisotropy field of the Mn${}_{2.6}$Co${}_{0.3}$Ga${}_{1.1}$ film, pulsed magnetic fields up to 60~T are used to determine the field strength required to saturate the film in the plane. For this, the extraordinary Hall effect was employed as a probe of the local magnetisation. By integrating the reconstructed in--plane magnetisation curve, the effective anisotropy energy density for Mn${}_{2.6}$Co${}_{0.3}$Ga${}_{1.1}$ is determined to be 1.23~MJ/m${}^3$.

arXiv commentJ. Phys. D (accepted)

References in corpus (6)

• Anomalous Hall effect
• High spin polarization in epitaxial films of ferrimagnetic Mn3Ga
• Loss of anisotropy in strained ultrathin epitaxial L10 Mn-Ga films
• Perpendicularly magnetized Mn-Co-Ga-based thin films with high coercive field
• Anomalous Hall Effect in perpendicularly magnetized Mn(_{3-x})Ga thin films
• Magnetic and transport properties of tetragonal- or cubic-Heusler-type Co-substituted Mn-Ga epitaxial thin films

Cited by in corpus (5)

• Helium Ion Microscopy for Reduced Spin Orbit Torque Switching Currents
• Magnetocrystalline anisotropy and exchange probed by high-field anomalous Hall effect in fully-compensated half-metallic Mn2RuxGa thin films
• Structure, site-specific magnetism and magneto-transport properties of epitaxial D0${}_{22}$ Mn${}_2$Fe${}_x$Ga thin films
• Tunnel magnetoresistance angular and bias dependence enabling tuneable wireless communication
• Titanium Nitride as a Seed Layer for Heusler Compounds