Optimization of a Non-arsenic Iron-based Superconductor for Wire Fabrication
arXiv:1412.3065 · doi:10.1088/0953-2048/28/4/045018
Abstract
We report on the optimization of synthesis of iron-selenide (non-arsenic) superconducting powders that are based on '122' composition, with optimal Tc = 38 K and Jc = 10^5 A/cm2 (4 K). We also report on the wire proof-of concept for these materials, by producing ~ 40 ft of wire that produce Ic. The 122 selenides are more difficult to synthesize and have more complex crystal structures compared to '11' selenides (FeSe and FeSe1-xTex), but they do offer higher Tc and might provoke a natural extension for 11 work.
13 pages, 7 figures; Submitted to SuST
References in corpus (16)
- Superconductivity at 38 K in the iron arsenide (Ba1-xKx)Fe2As2
- Superconductivity at 22 K in Co-doped BaFe2As2 Crystals
- Superconductivity up to 37 K in (A1-xSrx)Fe2As2 with A=K and Cs
- Superconductivity and Phase Diagram in the Iron-based Arsenic-oxides ReFeAsO1-delta (Re = rare earth metal) without F-Doping
- Thorium-doping induced superconductivity up to 56 K in Gd1-xThxFeAsO
- Nearly Isotropic superconductivity in (Ba,K)Fe2As2
- Fe-based high temperature superconductivity with Tc=31K bordering an insulating antiferromagnet in (Tl,K)FexSe2 Crystals
- Small anisotropy, weak thermal fluctuations, and high field superconductivity in Co-doped iron pnictide Ba(Fe1-xCox)2As2
- High intergrain critical current density in fine-grain (Ba0.6K0.4)Fe2As2 wires and bulks
- Fishtail effect and the vortex phase diagram of single crystal Ba0.6K0.4Fe2As2
- Critical Fields and Anisotropy of NdO0.82F0.18FeAs Single Crystals
- Superconducting Phases in Potassium-Intercalated Iron Selenides
- Hydrogen in layered iron arsenide: indirect electron doping to induce superconductivity
- NMR Study in the Iron-Selenide Rb0.74Fe1.6Se2: Determination of the Superconducting Phase as Iron Vacancy-Free Rb0.3Fe2Se2
- Superconductivity at Tc = 44 K in LixFe2Se2(NH3)y
- Cation vacancy order in the K0.8+xFe1.6-ySe2 system: five-fold cell expansion accommodates 20% tetrahedral vacancies