Tunable Cobalt Vacancies and Related Properties in LaCoxAs2
arXiv:1411.2788 · doi:10.1021/cm5029639
Abstract
The origin of transition metal vacancies and their effects on the properties of ThCr2Si2-type compounds have been less studied and poorly understood. Here we carefully investigate the structure, physical properties, and electronic structure for a series of lanthanum cobalt arsenides with nominal composition of LaCoxAs2 (1.6 < = x < = 2.1). It is revealed that the occupancy of Co can be tuned between 1.98(1) and 1.61(1). The structural analyses based on X-ray and neutron diffractions show the existence of Co vacancies results from charge balance due to the formation of bond between As-As. These Co vacancies affect the magnetic and electrical properties greatly, adjusting the Curie temperature from 205 to 47 K and increasing the resistivity by more than 100%. First principles calculations indicate that the Co vacancies weaken the spin polarization and reduce the density of states at the Fermi level, resulting in decreased Curie temperature and increased resistivity, respectively. Our results address the importance of transition metal vacancies in ThCr2Si2-type materials and offer a reliable route to tune the magnetism of ThCr2Si2-type structure.
10 pages, 4 figures
References in corpus (7)
- Superconductivity at 38 K in the iron arsenide (Ba1-xKx)Fe2As2
- Pressure-induced volume-collapsed tetragonal phase of CaFe2As2 as seen via neutron scattering
- Superconductivity in Co-doped LaFeAsO
- The Unprecedented Giant Coupling of Fe-spin State and the As-As Hybridization in Iron-Pnictide
- Lattice collapse and quenching of magnetism in CaFe2As2 under pressure: A single crystal neutron and x-ray diffraction investigation
- Superconducting Phases in Potassium-Intercalated Iron Selenides
- Itinerant Ferromagnetism in layered crystals LaCoOX (X = P, As)