Resistance noise at the metal-insulator transition in thermochromic VO2 films

Abstract

Thermochromic VO2 films were prepared by reactive DC magnetron sputtering onto heated sapphire substrates and were used to make 100-nm-thick samples that were 10 μm wide and 100 micron long. The resistance of these samples changed by a factor of about 2000 in the 50 < Ts < 70 C range of temperature Ts around the "critical" temperature Tc between a low-temperature semiconducting phase and a high-temperature metallic-like phase of VO2. Power density spectra S(f) were extracted for resistance noise around Tc and demonstrated unambiguous 1/f behavior. Data on S(10Hz)/Rs^2 scaled as Rs^x, where Rs is sample resistance; the noise exponent x was -2.6 for Ts < Tc and +2.6 for Ts > Tc. These exponents can be reconciled with the Pennetta-Trefan-Reggiani theory [C. Pennetta, G. Trefanan, and L. Reggiani, Phys. Rev. Lett. 85, 5238 (2000)] for lattice percolation with switching disorder ensuing from random defect generation and healing in steady state. Our work hence highlights the dynamic features of the percolating semiconducting and metallic-like regions around Tc in thermochromic VO2 films.

submitted for publication, this topic is condensed matter physics

References in corpus (4)

• Mott transition in VO2 revealed by infrared spectroscopy and nano-imaging
• Infrared spectroscopy and nano-imaging of the insulator-to-metal transition in vanadium dioxide
• Signature of persistent metallic domains in FORC measurements of the VO${}_2$ metal-insulator transition
• Surface versus bulk characterization of the electronic inhomogeneity in a VO_{2} film

Cited by in corpus (1)

• Thickness dependent transition from the 1T${}^{\prime }$ to Weyl semimetal phase in ultrathin MoTe${}_2$: Electrical transport, Noise and Raman studies