Structural and electronic properties of epitaxial YBaCuO/LaCaMnO bilayers grown on SrTiO${}_3$ (110) substrates

Abstract

Epitaxial bilayers of the high-temperature-superconductor YBa2Cu3O7-d (YBCO) and the ferromagnetic metal La0.67Ca0.33MnO3 (LCMO) were prepared by pulsed laser deposition on (110)-oriented SrTiO3 substrates, such that the CuO2 planes of YBCO are perpendicular to the YBCO-LCMO interface. X-ray diffraction and Raman scattering demonstrate complete (110) orientation of both YBCO and LCMO overlayers. The resistivity and magnetization of the bilayer films are highly anisotropic. The critical temperatures for superconductivity and ferromagnetism as well as the saturation magnetization exhibit modest reductions compared to corresponding bulk values.

References in corpus (4)

• Strain-driven elastic and orbital-ordering effects on thickness-dependent properties of manganite thin films
• Long-range transfer of electron-phonon coupling in oxide superlattices
• On Magnetic Interlayer Coupling and Proximity Effect in a La${}_{0.67}$Ca${}_{0.33}$MnO${}_3$(10 nm)/YBa${}_2$Cu${}_3$O${}_7$(10 nm) Superlattice
• Magnetoresistance studies of $L{a}_{2/3}S{r}_{1/3}Mn{O}_3$ - $YB{a}_{2}C{u}_3{O}_7$ - $L{a}_{2/3}S{r}_{1/3}Mn{O}_3$ trilayers with ferromagnetic coupling along the nodal direction of $YB{a}_{2}C{u}_3{O}_7$