Role of MgO impurity on the superconducting properties of MgB2

Abstract

We address the effect of MgO impurity on the superconducting properties of MgB2. The synthesis of MgB2 is very crucial because of sensitivity of Mg to oxidation which may lead to MgO as a secondary phase. Rietveld refinement was performed to determine the quantitative volume fraction of MgO in the samples synthesized by two different techniques. Both the samples were subjected to magnetization measurements under dc and ac applied magnetic fields and the observed results were compared as a function of temperature. Paramagnetic Meissner effect has been observed in a sample of MgB2 having more amount of MgO (with Tc = 37.1K) whereas the pure sample MgB2 having minor quantity of MgO shows diamagnetic Meissner effect with Tc = 38.8K. M-H measurements at 10K reveal a slight difference in irreversibility field which is due to MgO impurity along with wide transition observed from ac magnetic susceptibility measurements. The magnetotransport measurements R(T)H using RN = 90%, 50% and 10% criterion on pure sample of MgB2 has been used to determine the upper critical field whereas the sample having large quantity of MgO does not allow these measurements due to its high resistance.

arXiv comment15 pages text + Figs

References in corpus (10)

• Strongly linked current flow in polycrystalline forms of the new superconductor MgB2
• Enhancement of the critical current density and flux pinning of MgB2 superconductor by nanoparticle SiC doping
• Enhancement of the upper critical field by nonmagnetic impurities in dirty two-gap superconductors
• Superconducting Properties of MgB2 Bulk Materials Prepared by High Pressure Sintering
• Very high upper critical fields in MgB2 produced by selective tuning of impurity scattering
• Type-1.5 Superconductors
• Nanoscale-SiC doping for enhancing Jc and Hc2 in the Superconducting MgB2
• High-pressure synthesis of pure and doped superconducting MgB2 compounds
• Effect of synthesis temperature on superconducting properties of n-SiC added bulk MgB2 superconductor
• Physical property characterization of Fe-tube encapsulated and vacuum annealed bulk MgB2

Cited by in corpus (3)

• Reinforcing increase of ΔTC in MgB2 smart meta-superconductors by adjusting the concentration of inhomogeneous phases
• Smart meta-superconductor MgB2 constructed by inhomogeneous phase of luminescent nanocomposite
• Establishment of global phase coherence in a highly disordered fractal MgO/MgB2 nanocomposite: Roles of interface, morphology and defect