Evolution of superconductivity in PrFe1-xCoxAsO with x = 0.0 to 1.0

Abstract

We report the synthesis and physical property characterization of PrFe1-xCoxAsO with x = 0.0 to 1.0. The studied samples are synthesized by solid state reaction route via vacuum encapsulation method. The pristine compound PrFeAsO does not show superconductivity, but rather exhibits a metallic step like transition due to spin density wave ordering of Fe moments below 150 K, followed by another upward step due to anomalous ordering of Pr moments at 12 K. Both the Fe-SDW and Pr-TN temperatures decrease monotonically with Co substitution at Fe site. Superconductivity appears in a narrow range of x from 0.07 to 0.25 with maximum Tc at 11.12 K for x = 0.15. Samples, with x = 0.25 exhibit metallic behavior right from 300 K down to 2 K, without any Fe-SDW or Pr-TN steps in resistivity. In fact, though Fe-SDW decreases monotonically, the Pr-TN is disappeared even with x = 0.02. The magneto transport measurements below 14 Tesla on superconducting polycrystalline Co doped PrFeAsO lead to extrapolated values of the upper critical fields [Hc2(0)] of up to 60 Tesla.

15 pages Text+Figs

References in corpus (11)

• Superconductivity at 43 K in Samarium-arsenide Oxides $SmFeAs{O}_{1-x}{F}_x$
• Superconductivity at 41 K and its competition with spin-density-wave instability in layered CeO${}_{1-x}$F${}_x$FeAs
• Superconductivity in iron-based F-doped layered quaternary compound Nd[O1-xFx]FeAs
• Superconductivity at 52 K in iron-based F-doped layered quaternary compound Pr[O1-xFx]FeAs
• Upper critical fields and thermally-activated transport of Nd(O_0.7F_0.3)FeAs single crystal
• Superconductivity in Co-doped LaFeAsO
• Superconductivity at 36 K in Gadolinium-arsenide Oxides GdO${}_{1-x}$F${}_x$FeAs
• Magnetic Ordering and Negative Thermal Expansion in PrFeAsO
• Superconductivity above 50 K in Tb${}_{1-x}$Th${}_x$FeAsO
• Superconductivity in Co-doped SmFeAsO
• Superconductivity at 11.3 K induced by cobalt doping in CeOFeAs