Photo-induced persistent inversion of germanium in a 200-nm-deep surface region

Abstract

The controlled manipulation of the charge carrier concentration in nanometer thin layers is the basis of current semiconductor technology and of fundamental importance for device applications. Here we show that it is possible to induce a persistent inversion from n- to p-type in a 200-nm-thick surface layer of a germanium wafer by illumination with white and blue light. We induce the inversion with a half-life of ~12 hours at a temperature of 220 K which disappears above 280 K. The photo-induced inversion is absent for a sample with a 20-nm-thick gold capping layer providing a Schottky barrier at the interface. This indicates that charge accumulation at the surface is essential to explain the observed inversion. The contactless change of carrier concentration is potentially interesting for device applications in opto-electronics where the gate electrode and gate oxide could be replaced by the semiconductor surface.

Cited by in corpus (4)

• The new high field photoexcitation muon spectrometer at the ISIS pulsed neutron and muon source
• A segmented conical electric lens for optimization of the beam spot of the low-energy muon facility at PSI: a Geant4 simulation analysis
• Direct observation of hole carrier density profiles and their light induced manipulation at the surface of Ge
• Muon probes of temperature-dependent charge carrier kinetics in semiconductors