Photoluminescence in amorphous MgSiO_3 silicate
arXiv:1307.0649 · doi:10.1093/mnras/stt1203
Abstract
Samples of amorphous MgSiO_3 annealed at temperature steps leading up to their crystallisation temperature show a rise in photoluminescence activity, peaking at ~450C. The photoluminescence band has a main peak at 595nm and a weaker peak at 624nm. We present laboratory data to show that the maximum in photoluminescence activity is related to substantial structural reordering that occurs within a relatively narrow temperature range. We attribute the origin of the photoluminescence to non-bridging oxygen hole centre defects, which form around ordered nano-sized domain structures as a result of the breakup of tetrahedral connectivity in the disordered inter-domain network, aided by the loss of bonded OH. These defects are removed as crystallisation progresses, resulting in the decrease and eventual loss of photoluminescence. Thermally processed hydrogenated amorphous silicate grains could therefore represent a potential carrier of extended red emission.
arXiv comment12 pages, 12 figs. Accepted for publication in MNRAS
References in corpus (10)
- Interstellar Dust Grains
- Detection of Extended Red Emisson in the Diffuse Interstellar Medium
- Silicon Nanoparticles: Source of Extended Red Emission?
- The Excitation of Extended Red Emission: New Constraints on its Carrier From HST Observations of NGC 7023
- Forsterite Amorphisation by Ion Irradiation: Monitoring by Infrared Spectroscopy
- Extended Red Emission in High-Galactic Latitude Interstellar Clouds
- Optical Spectroscopy of Galactic Cirrus Clouds: Extended Red Emission in the Diffuse Interstellar Medium
- The Photophysics of the Carrier of Extended Red Emission
- Extended Red Emission and the evolution of carbonaceaous nanograins in NGC 7023
- Photo-Luminescence and Possible Forsterite nanoparticles Model of Extended Red Emission