Experimental study of the effect of disorder on subcritical crack growth dynamics

Abstract

The growth dynamics of a single crack in a heterogeneous material under subcritical loading is an intermittent process; and many features of this dynamics have been shown to agree with simple models of thermally activated rupture. In order to better understand the role of material heterogeneities in this process, we study the subcritical propagation of a crack in a sheet of paper in the presence of a distribution of small defects such as holes. The experimental data obtained for two different distributions of holes are discussed in the light of models that predict the slowing down of crack growth when the disorder in the material is increased; however, in contradiction with these theoretical predictions, the experiments result in longer lasting cracks in a more ordered scenario. We argue that this effect is specific to subcritical crack dynamics and that the weakest zones between holes at close distance to each other are responsible both for the acceleration of the crack dynamics and the slightly different roughness of the crack path.

4 pages, 5 figures, accepted in Physical Review Letters (http://prl.aps.org)

References in corpus (8)

• Failure Processes in Elastic Fiber Bundles
• Role of disorder in the size-scaling of material strength
• Crack propagation through phase separated glasses: effect of the characteristic size of disorder
• Creep of a fracture line in paper peeling
• Discrepancy between sub-critical and fast rupture roughness: a cumulant analysis
• Slow Crack Propagation in Heterogeneous Materials
• The cooperative effect of load and disorder in thermally activated rupture of a two-dimensional random fuse network
• Super-Arrhenius dynamics for sub-critical crack growth in disordered brittle media

Cited by in corpus (7)

• Opto-Nanomechanics Strongly Coupled to a Rydberg Superatom: Coherent vs. Incoherent Dynamics
• Record statistics of bursts signals the onset of acceleration towards failure
• Record breaking bursts in a fiber bundle model of creep rupture
• Creep rupture as a non-homogeneous Poissonian process
• System-size-dependent avalanche statistics in the limit of high disorder
• Blending stiffness and strength disorder can stabilize fracture
• Impact induced transition from damage to perforation