Artificial and self-assembled pinning centers in Ba(Fe1-xCox)2As2 thin films as a route to very high current density

Abstract

We report on the superior vortex pinning of single and multilayer Ba(Fe1-xCox)2As2 thin films with self-assembled c-axis and artificially introduced ab-plane pins. Ba(Fe1-xCox)2As2 can accept a very high density of pins (15-20 vol%) without Tc suppression. The matching field is greater than 12 T, producing a significant enhancement of the critical current density Jc, an almost isotropic Jc (Theta,20T) > 10^5 A/cm2, and global pinning force density Fp of about 50 GN/m^3. This scenario strongly differs from the high temperature cuprates where the addition of pins without Tc suppression is limited to 2-4 vol%, leading to small HIrr enhancements and improved Jc only below 3-5 Tesla.

20 pages,8 figures. Accepted for publication in Physical Review B

References in corpus (12)

• Superconductivity at 38 K in the iron arsenide (Ba1-xKx)Fe2As2
• Superconductivity at 43 K in Samarium-arsenide Oxides $SmFeAs{O}_{1-x}{F}_x$
• Thorium-doping induced superconductivity up to 56 K in Gd1-xThxFeAsO
• Very High Field Two-Band Superconductivity in LaFeAsO_0.89F_0.11
• Nearly Isotropic superconductivity in (Ba,K)Fe2As2
• Small anisotropy, weak thermal fluctuations, and high field superconductivity in Co-doped iron pnictide Ba(Fe1-xCox)2As2
• A general scaling relation for the critical current density in Nb3Sn
• Evidence for two distinct scales of current flow in polycrystalline Sm and Nd iron oxypnictides
• Psuedo-isotropic upper critical field in cobalt-doped SrFe2As2 epitaxial films
• Strong Tc dependence for strained, epitaxial Ba(Fe1-xCox)2As2 thin films
• Superconductivity in Epitaxial Thin Films of Co-Doped SrFe2As2 with Bilayered FeAs Structures and their Magnetic Anisotropy
• Evidence for electromagnetic granularity in the polycrystalline iron-based superconductor LaO0.89F0.11FeAs