Calculation of the transport critical current density of c-axis textured 122 iron-based superconductors

Abstract

The c-axis textured Sr1-xKxFe2As2 tapes produced by cold rolling and post-annealing, could carry a high super-current over 2*104 A/cm2. However, the magnitude is far from its maximum, because of the current obstacles associated with various defects in the material. To predict the maximal transport critical current density, we modeled the current paths in a c-axis textured polycrystal as a three-dimensional flow network, and calculated the maximum flow with the Ford-Fulkerson algorithm. It indicates that a much higher super-current of about 2*105 A/cm2 could be achieved in an ideal c-axis textured K-doped 122 polycrystal. The dependences of transport Jc on density, content of invalid boundary and grain size and shape were also studied. The results imply that, over 30% of the grain boundaries in the reported c-axis textured Sr1-xKxFe2As2 tapes may act as current obstacles, and the large ratio of width to thickness was expected to be the most favorable grain shape for high transport Jc in c-axis textured 122 superconducting tapes.

17 pages, 7 figures

References in corpus (9)

• Superconductivity at 38 K in the iron arsenide (Ba1-xKx)Fe2As2
• Advantageous grain boundaries in iron pnictide superconductors
• Upper critical fields well above 100 T for the superconductor SmFeAsO${}_{0.85}$F${}_{0.15}$ with T${}_c$ = 46 K
• Evidence for two distinct scales of current flow in polycrystalline Sm and Nd iron oxypnictides
• Fabrication of the iron-based superconducting wire using Fe(Se, Te)
• Intrinsic magnetic properties of NdFeAsO${}_{0.9}$F${}_{0.1}$ superconductor from local and global measurements
• High transport critical current densities in textured Fe-sheathed Sr1-xKxFe2As2+Sn superconducting tapes
• Structural and critical current properties in polycrystalline SmO1-xFxFeAs
• Evidence for Supercurrent Connectivity in Conglomerate Particles in NdFeAsO1-d