Local deformations and incommensurability of high quality epitaxial graphene on a weakly interacting transition metal

Abstract

We investigate the fine structure of graphene on iridium, which is a model for graphene weakly interacting with a transition metal substrate. Even the highest quality epitaxial graphene displays tiny imperfections, i.e. small biaxial strains, ca. 0.3%, rotations, ca. 0.5^{\circ}, and shears over distances of ca. 100 nm, and is found incommensurate, as revealed by X-ray diffraction and scanning tunneling microscopy. These structural variations are mostly induced by the increase of the lattice parameter mismatch when cooling down the sample from the graphene preparation temperature to the measurement temperature. Although graphene weakly interacts with iridium, its thermal expansion is found positive, contrary to free-standing graphene. The structure of graphene and its variations are very sensitive to the preparation conditions. All these effects are consistent with initial growth and subsequent pining of graphene at steps.

References in corpus (5)

• Control and Characterization of Individual Grains and Grain Boundaries in Graphene Grown by Chemical Vapor Deposition
• Dirac Cones and Minigaps for Graphene on Ir(111)
• Finite temperature lattice properties of graphene beyond the quasiharmonic approximation
• Magnetism in Disordered Graphene and Irradiated Graphite
• Unit cell of graphene on Ru(0001): a 25 x 25 supercell with 1250 carbon atoms

Cited by in corpus (5)

• Epitaxial hexagonal boron nitride on Ir(111): A work function template
• Topography of the graphene/Ir(111) moir{é} studied by surface x-ray diffraction
• Decoupling Molybdenum Disulfide from its Substrate by Cesium Intercalation
• Elastic properties of moiré lattices in epitaxial two-dimensional materials
• Moiré induced organization of size-selected Pt clusters soft landed on epitaxial graphene