Properties of Binary Transition-Metal Arsenides (TAs)

Abstract

We present thermodynamic and transport properties of transition-metal (T) arsenides, TAs with T = Sc to Ni (3d), Zr, Nb, Ru (4d), Hf and Ta (5d). Characterization of these binaries is made with powder X-ray diffraction, temperature and field-dependent magnetization and resistivity, temperature-dependent heat capacity, Seebeck coefficient, and thermal conductivity. All binaries show metallic behavior except TaAs and RuAs. TaAs, NbAs, ScAs and ZrAs are diamagnetic, while CoAs, VAs, TiAs, NiAs and RuAs show approximately Pauli paramagnetic behavior. FeAs and CrAs undergo antiferromagnetic order below TN = 71 K and TN \approx 260 K, respectively. MnAs is a ferromagnet below TC = 317 K and undergoes hexagonal-orthorhombic-hexagonal transitions at TS = 317 K and 384 K, respectively. For TAs, Seebeck coefficients vary between + 40 uV/K and - 40 uV/K in the 2 K to 300 K range, whereas thermal conductivity values stay below 18 W/(m K). The Sommerfeld-coefficient γ are less than 10 mJ/(K2mol). At room temperature with application of 8 Tesla magnetic field, large positive magnetoresistance is found for TaAs (~25%), MnAs (~90%) and for NbAs (~75%).

7 figures; Will be published in the upcoming focus issue in Superconductor Science and Technology

References in corpus (8)

• Superconductivity at 27 K in tetragonal FeSe under high pressure
• Superconductivity and Phase Diagram in the Iron-based Arsenic-oxides ReFeAsO1-delta (Re = rare earth metal) without F-Doping
• Thorium-doping induced superconductivity up to 56 K in Gd1-xThxFeAsO
• Superconductivity under high pressure in LaFeAsO
• Electronic structure and Magnetism in BaMn${}_2$As${}_2$ and BaMn${}_2$Sb${}_2$
• Hydrogen in layered iron arsenide: indirect electron doping to induce superconductivity
• Itinerant antiferromagnetism in BaCr${}_2$As${}_2$
• Non-collinear spin-density wave antiferromagnetism in FeAs