Local Structure of the Superconductor K0.8Fe1.6+xSe2: Evidence of Large Structural Disorder

Abstract

The local structure of superconducting single crystals of K0.8Fe1.6+xSe2 with Tc = 32.6 K was studied by x-ray absorption spectroscopy. Near-edge spectra reveal that the average valence of Fe is 2+. The room temperature structure about the Fe, K and Se sites was examined by iron, selenium and potassium K-edge measurements. The structure about the Se and Fe sites shows a high degree of order in the nearest neighbor Fe-Se bonds. On the other hand, the combined Se and K local structure measurements reveal a very high level of structural disorder in the K layers. Temperature dependent measurements at the Fe sites show that the Fe-Se atomic correlation follows that of the Fe-As correlation in the superconductor LaFeAsO0.89F0.11 - having the same effective Einstein temperature (stiffness). In K0.8Fe1.6+xSe2, the nearest neighbor Fe-Fe bonds has a lower Einstein temperature and higher structural disorder than in LaFeAsO0.89F0.11. The moderate Fe site and high K site structural disorder is consistent with the high normal state resistivity seen in this class of materials. For higher shells, an enhancement of the second nearest neighbor Fe-Fe interaction is found just below Tc and suggests that correlations between Fe magnetic ion pairs beyond the first neighbor are important in models of magnetic order and superconductivity in these materials.

References in corpus (9)

• Superconductivity at 38 K in the iron arsenide (Ba1-xKx)Fe2As2
• High-temperature superconductivity in iron-based materials
• The superconductivity at 18 K in LiFeAs system
• Superconductivity and Phase Diagram in the Iron-based Arsenic-oxides ReFeAsO1-delta (Re = rare earth metal) without F-Doping
• To What Extent Iron-Pnictide New Superconductors Have Been Clarified: A Progress Report
• Nanoscale phase separation in the iron chalcogenide superconductor K0.8Fe1.6Se2 as seen via scanning nanofocused x-ray diffraction
• Intrinsic phase separation in superconducting K0.8Fe1.6Se2 (Tc= 31.8 K) single crystals
• Evidence of local structural inhomogeneity in FeSe(1-x)Te(x) from extended x-ray absorption fine structure
• Superconductivity on the verge of Mott localization in ternary iron sulfide

Cited by in corpus (7)

• Coexistence of different electronic phases in the K0.8Fe1.6Se2 superconductor: a bulk-sensitive hard x-rays spectroscopy study
• Large local disorder in the superconducting K_{0.8}Fe_{1.6}Se_{2} studied by extended x-ray absorption fine structure
• Interplay of the electronic and lattice degrees of freedom in A_{1-x}Fe_{2-y}Se_{2} superconductors under pressure
• Competing striped structures in La2CuO4+y
• $\mathrm{L}{\mathrm{i}}_{\mathrm{x}}({\mathrm{C}}_5{\mathrm{H}}_5\mathrm{N}{)}_{\mathrm{y}}\mathrm{F}{\mathrm{e}}_{2-\mathrm{z}}\mathrm{S}{\mathrm{e}}_2$: a defect resilient expanded-lattice high-temperature superconductor
• Suppression of the antiferromagnetic order when approaching the superconducting state in a phase-separated crystal of K${}_x$Fe${}_{2-y}$Se${}_2$
• Two-particle excitations under coexisting electron interaction and disorder