Mössbauer studies of powdered single crystals of FeTe0.5Se0.5

Abstract

The Mössbauer measurements performed on powdered single crystals of FeTe0.5Se0.5 (Tc ~ 14.7 K) reveal minor content of two impurity phases, identified as Fe3O4 and Fe7Se8, among the major tetragonal phase. From the shape of impurity subspectra it follows that Fe7Se8 behaves in superparamagnetic manner, most likely because of randomly distributed Fe vacancies in the lattice structure of Fe Te Se. The magnetite content in the powdered absorber exposed to ambient air conditions remains unchanged during period of 16 months. Ageing effects were observed for the samples stored under argon atmosphere and small increase of the isomer shift of the doublet was detected. Presented temperature dependence of the hyperfine parameters can be explained as due to possible orthorhombic distortion or to temperature behaviour of impurity phases Fe3O4 and Fe7Se8. Strong tendency to formation of crystalline texture of powdered sample is observed.

13 pages, 8 figures

References in corpus (19)

• Superconductivity at 36 K in beta-Fe1.01Se with the compression of the interlayer separation under pressure
• Spin density wave anomaly at 140 K in the ternary iron arsenide BaFe2As2
• Extreme Sensitivity of Superconductivity to Stoichiometry in FeSe (Fe1+dSe)
• Superconductivity close to magnetic instability in Fe(Se1-xTex)0.82
• Tellurium substitution effect on superconductivity of the alpha-phase Iron Selenide
• Incommensurate magnetic order in the alpha-Fe(Te,Se) superconductor systems
• First-order magnetic and structural phase transitions in Fe${}_{1+y}$Se${}_x$Te${}_{1-x}$
• Substitution Effects on FeSe Superconductor
• Crystal structure of the new FeSe1-x superconductor
• Anisotropic superconducting properties of single-crystalline FeSe0.5Te0.5
• Investigation of the spin-glass regime between the antiferromagnetic and superconducting phases in Fe${}_{1+y}$Se${}_x$Te${}_{1-x}$
• The Stoichiometry of FeSe
• Physical properties of FeSe${}_{0.5}$Te${}_{0.5}$ single crystals grown under different conditions
• Spin Ordering in LaOFeAs and Its Suppression in Superconductor LaO0.89F0.11FeAs Probed by Mössbauer Spectroscopy
• Metal - Insulator transition in Fe1.01-xCuxSe
• Growth conditions, structure, and superconductivity of pure and metal-doped FeTe1-xSex single crystals
• Short-range incommensurate magnetic order near the superconducting phase boundary in Fe(1+d)Te(1-x)Se(x)
• Moessbauer spectroscopy evidence for the lack of iron magnetic moment in superconducting FeSe
• Observation of lattice softening at $T_{\mathrm{c}}$ in the FeSe${}_{0.5}$Te${}_{0.5}$ superconductor

Cited by in corpus (3)

• Microstructural magnetic phases in superconducting FeTe0.65Se0.35
• The substitution effects on electronic structure of iron selenide superconductors
• Microstructural and transport properties of superconducting FeTe0.65Se0.35 crystals