Unusual Phase Transitions and Magnetoelastic Coupling in TlFe1.6Se2 Single Crystals

Abstract

Structural, magnetic, electrical transport, and heat capacity data are reported for single crystals of TlFe1.6Se2. This compound crystallizes in a tetragonal structure similar to the ThCr2Si2 structure, but with vacancies in the Fe layer. The vacancies can be ordered or disordered depending on temperature and thermal history. If the vacancies are ordered, the basal plane lattice constant increases from a to \sqrt{5}a. Antiferromagnetic order with the Fe spins along the c-axis occurs below T_N ~ 430K as shown by single crystal neutron diffraction and the magnetic structure is reported. In addition, for the vacancy ordered crystal, two other phase transitions are found at T_1 ~ 140K, and T_2 ~ 100K. The phase transitions at T_1 and T_2 are evident in heat capacity, magnetic susceptibility, resistivity data, a and c lattice parameters, and in the unusual temperature dependence of the magnetic order parameter determined from neutron scattering. The phase transitions at T_1 and T_2 result in significant changes in the magnetic moment per iron, with 1.72(6)μ_B observed at 300K, 2.07(9)μ_B at 140\,K, 1.90(9)\,μ_B at 115\,K, and 1.31(8)μ_B for 5\,K if the same "block checkerboard" magnetic structure is used at all temperatures. The phase transitions appear to be driven by small changes in the c lattice constant, large magnetoelastic coupling, and the localization of carriers with decreasing temperature.

Accepted for publication in Physical Review B

References in corpus (6)

• Superconductivity at 22 K in Co-doped BaFe2As2 Crystals
• Fe-based high temperature superconductivity with Tc=31K bordering an insulating antiferromagnet in (Tl,K)FexSe2 Crystals
• Superconductivity at 32 K in single crystal Rb${}_{0.78}$Fe${}_2$Se${}_{1.78}$}
• Synthesis and crystal growth of Cs0.8(FeSe0.98)2: a new iron-based superconductor with Tc=27K
• Electronic Structure of Fe-Based Superconductors
• Density Functional Study of the Over-Doped Iron Chalcogenide: TlFe${}_2$Se${}_2$ with ThCr${}_2$Si${}_2$ structure

Cited by in corpus (10)

• Superconductivity in Iron Compounds
• Iron-Based Superconductors: current status of materials and pairing mechanism
• Phase relations in K_xFe_{2-y}Se_2 and the structure of superconducting K_xFe_2Se_2 via high-resolution synchrotron diffraction
• Anisotropic magnetism, superconductivity, and the phase diagram of Rb(1-x)Fe(2-y)Se2
• Electric double-layer transistor using layered iron selenide Mott insulator TlFe1.6Se2
• Spin reorientation in TlFe1.6Se2 with complete vacancy ordering
• Intertwined magnetic and nematic orders in semiconducting KFe${}_{0.8}$Ag${}_{1.2}$Te${}_2$
• Evolution of the nuclear and magnetic structures of TlFe1.6Se2 with temperature
• Exploration of iron-chalcogenide superconductors
• Pressure-induced magnetic collapse and metallization of $\mathrm{TlF}{\mathrm{e}}_{1.6}\mathrm{S}{\mathrm{e}}_2$