Effect of size reduction on the ferromagnetism of the manganite La1-xCaxMnO3 (x = 0.33)

Abstract

In this paper we report an investigation on the ferromagnetic state and the nature of ferromagnetic transition of nanoparticles of $\mathrm{L}{\mathrm{a}}_{0.67}\mathrm{C}{\mathrm{a}}_{0.33}\mathrm{Mn}{\mathrm{O}}_3$ using magnetic measurements and neutron diffraction. The investigation was made on nanoparticles with crystal size down to $15$ nm. The neutron data show that even down to a size of $15$ nm the nanoparticles show finite spontaneous magnetization ($M_S$) although the value is much reduced compared to the bulk sample. We observed a non-monotonic variation of the ferromagnetic to paramagnetic transition temperature $T_C$ with size $d$ and found that $T_C$ initially enhances on size reduction, but for $d<50$ nm it decreases again. The initial enhancement in $T_C$ was related to an increase in the bandwidth that occured due to a compaction of the Mn-O bond length and a straightening of the Mn-O-Mn bond angle, as determined form the neutron data. The size reduction also changes the nature of the ferromagnetic to paramagnetic transition from first order to second order with critical exponents approaching mean field values. This was explained as arising from a truncation of the coherence length by the finite sample size.

12 figures

References in corpus (2)

• Crystal structure and physical properties of half-doped manganite nanocrystals with size < 100nm
• Experimental observation of charge ordering in nanocrystalline Pr${}_{0.65}$Ca${}_{0.35}$MnO${}_3$

Cited by in corpus (3)

• Growth and physical property study of single nanowire (diameter ~ 45nm) of half doped Manganite
• Critical behavior and magnetic relaxation dynamics of Nd0.4Sr0.6MnO3 nanoparticles
• Electrical transport properties of nanostructured ferromagnetic perovskite oxides La_0.67Ca_0.33MnO_3 and La_0.5Sr_0.5CoO_3 at low temperatures (5 K > T >0.3 K) and high magnetic field