Striking Zn impurity effect on the Fe-based superconductor BaFe1.87Co0.13As2

Abstract

Nonmagnetic impurity effect was studied on the n-type Fe-based superconductor BaFe1.87Co0.13As2 (Tc = 25 K) by a successful Zn substitution for Fe up to 7 at.%. Magnetic susceptibility, electrical resistivity, specific heat, and Hall coefficient measurements indicated that Tc linearly decreases with the Zn concentration and disappears at 7 at.%. The result is quantitatively comparable with what was observed for YBCO, while it disagrees with a recent report for the p-type Ba0.5K0.5Fe2As2. Fragile SC against a nonmagnetic impurity was first confirmed for the n-type 122 Fe-based superconductor.

14 pages, 5 figures

References in corpus (15)

• Unconventional sign-reversing superconductivity in LaFeAsO_(1-x)F_x
• Superconductivity at 43 K in Samarium-arsenide Oxides $SmFeAs{O}_{1-x}{F}_x$
• Unconventional pairing originating from disconnected Fermi surfaces in superconducting LaFeAsO${}_{1-x}$F${}_x$}
• Superconductivity at 22 K in Co-doped BaFe2As2 Crystals
• Spin density wave anomaly at 140 K in the ternary iron arsenide BaFe2As2
• Superconductivity in SrFe_(2-x)Co_xAs_2: Internal Doping of the Iron Arsenide Layers
• Superconductivity induced by doping Pd in SrFe2-xPdxAs2
• Superconductivity at 22.3 K in SrFe2-xIrxAs2
• Superconductivity and phase diagrams in 4d- and 5d-metal-doped iron arsenides SrFe_{2-x}M_xAs_2 (M = Rh, Ir, Pd)
• Tailoring the Superconductivity and Antiferromagnetic Order in SrFe2-xRhxAs2
• Valley density-wave and multiband superconductivity in Fe-pnictides
• Narrow superconducting window in Ni-doped LaFeAsO
• Superconductivity induced by ruthenium substitution in an iron arsenide: investigation of SrFe2-xRuxAs2 (0 <= x <= 2)
• Contrasting Pair-Breaking Effects by Doping Mn and Zn in Ba0.5K0.5Fe2As2
• Large decrease in the critical temperature of superconducting LaFeAsO0.85 compounds doped with 3% atomic weight of nonmagnetic Zn impurities

Cited by in corpus (5)

• Superconductivity suppression of Ba0.5K0.5Fe2-2xM2xAs2 single crystals by substitution of transition-metal (M = Mn, Ru, Co, Ni, Cu, and Zn)
• Linear decrease of critical temperature with increasing Zn substitution in the iron-based superconductor BaFe1.89-2xZn2xCo0.11As2
• Different effects of Ni and Co substitution on the transport properties of BaFe2As2
• Progress in nonmagnetic impurity doping studies on Fe-based superconductors
• Effects of the vortices and impurities on the nuclear spin relaxation rate in iron-based superconductors