Consequences of the peculiar intrinsic properties of MgB2 on its macroscopic current flow

Abstract

The influence of two important features of magnesium diboride on the macroscopic transport properties of polycrystalline MgB2 is discussed in the framework of a percolation model. While two band superconductivity does not have significant consequences in the field and temperature range of possible power applications, the opposite is true for the anisotropy of the upper critical field. The field dependence of the critical current densities strongly increases and the macroscopic supercurrents disappear well below the apparent upper critical field. The common scaling laws for the field dependence of the volume pinning force are altered and Kramer's plot is no longer linear, although grain boundary pinning dominates in nearly all polycrystalline MgB2 conductors. In contrast to the conventional superconductors NbTi and Nb3Sn, a significant critical current anisotropy can be induced by the preparation technique of MgB2 tapes.

References in corpus (9)

• Very high upper critical fields in MgB2 produced by selective tuning of impurity scattering
• Electronic Structure, Electron-Phonon Coupling, and Multiband Effects in MgB2
• Current percolation and anisotropy in polycrystalline MgB${}_2$
• Neutron Irradiation of Mg11B2 : From the Enhancement to the Suppression of Superconducting Properties
• Influence of the upper critical field anisotropy on the transport properties of polycrystalline MgB${}_2$
• Intraband versus interband scattering rate effects in neutron irradiated MgB2
• Anisotropy and internal field distribution of MgB2 in the mixed state at low temperatures
• Theory of the critical current in two-band superconductors with application to MgB2
• Critical currents in weakly textured MgB2: Nonlinear transport in anisotropic heterogeneous media