The role of silver addition on the structural and superconducting properties of polycrystalline Sr0.6K0.4Fe2As2

Abstract

The effect of Ag addition (0-20 wt%) on polycrystalline Sr0.6K0.4Fe2As2 superconductor has been investigated. It is found that the critical transition temperature Tc was not depressed, and the irreversibility field Hirr and hysteresis magnetization were significantly enhanced upon Ag addition. Characterization study reveals that larger grains are observed in the Ag-added samples. Moreover, the formation of glassy phase as well as amorphous layer, which are present in almost all the grain edges and boundaries in pure samples, are suppressed by Ag addition. The improvement of superconducting properties in Ag-added samples may originate from the enlargement of grains as well as better connections between grains

17 pages, 7 figures. Supercond. Sci. Technol.,accepted

References in corpus (7)

• Superconductivity at 38 K in the iron arsenide (Ba1-xKx)Fe2As2
• Superconductivity up to 37 K in (A1-xSrx)Fe2As2 with A=K and Cs
• Anisotropic thermodynamic and transport properties of single crystalline (Ba${}_{1-x}$K${}_x$)Fe${}_2$As${}_2$ (x = 0 and 0.45)
• Small anisotropy, weak thermal fluctuations, and high field superconductivity in Co-doped iron pnictide Ba(Fe1-xCox)2As2
• Transport and anisotropy in single-crystalline SrFe${}_2$As${}_2$ and $A_{0.6}$K${}_{0.4}$Fe${}_2$As${}_2$ ($A$ = Sr, Ba) superconductors
• Upper critical fields well above 100 T for the superconductor SmFeAsO${}_{0.85}$F${}_{0.15}$ with T${}_c$ = 46 K
• Evidence for Supercurrent Connectivity in Conglomerate Particles in NdFeAsO1-d

Cited by in corpus (6)

• Recent advances in iron-based superconductors toward applications
• The behavior of grain boundaries in the Fe-based superconductors
• Large Transport Critical Current Densities of Ag Sheathed (Ba,K)Fe2As2+Ag Superconducting Wires Fabricated by an ex-situ Powder-in-Tube (PIT) Process
• Development of Powder-in-Tube Processed Iron Pnictide Wires and Tapes
• Strongly enhanced current densities in Sr0.6K0.4Fe2As2 superconducting tapes
• Influence of Pb addition on the superconducting properties of polycrystalline Sr0.6K0.4Fe2As2