Superconductivity at 23 K and Low Anisotropy in Rb-Substituted BaFe_2As_2 Single Crystals

Abstract

Single crystals of Ba_{1-x}Rb_{x}Fe_2As_2 with x=0.05-0.1 have been grown from Sn flux and are bulk superconductors with T_c up to 23 K. The crystal structure was determined by X-ray diffraction analysis, and Sn is found to be incorporated for 9% Ba, shifted by 1.1 Angstroem away from the Ba site towards the (Fe_2As_2)-layers. The upper critical field deduced from resistance measurements is anisotropic with slopes of 7.1(3) T/K (H || ab-plane) and 4.2(2) T/K (H || c-axis), sufficiently far below T_c. The extracted upper critical field anisotropy of 3 close to T_c, is in good agreement with the estimate from magnetic torque measurements. This indicates that the electronic properties in the doped BaFe_2As_2 compound are significantly more isotropic than those in the LnFeAsO family. The in-plane critical current density at 5 K exceeds 10^6 A/cm^2, making Ba_{1-x}Rb_xFe_2As_2 a promising candidate for technical applications.

accepted for publication in Phys. Rev. B (9 pages, 11 figures)

References in corpus (18)

• Superconductivity at 38 K in the iron arsenide (Ba1-xKx)Fe2As2
• Spin density wave anomaly at 140 K in the ternary iron arsenide BaFe2As2
• Superconductivity up to 37 K in (A1-xSrx)Fe2As2 with A=K and Cs
• Thorium-doping induced superconductivity up to 56 K in Gd1-xThxFeAsO
• Very High Field Two-Band Superconductivity in LaFeAsO_0.89F_0.11
• Superconductivity at 25 K in hole doped $(L{a}_{1-x}S{r}_x)OFeAs$
• Superconductivity up to 29 K in SrFe2As2 and BaFe2As2 at high pressures
• Superconductivity and Crystal Structures of (Ba1-xKx)Fe2As2 (x = 0 - 1)
• Coexistence of the spin-density-wave and superconductivity in the (Ba,K)Fe2As2
• Upper critical fields and thermally-activated transport of Nd(O_0.7F_0.3)FeAs single crystal
• Superconductivity induced by Ni doping in BaFe${}_2$As${}_2$
• Fishtail effect and the vortex phase diagram of single crystal Ba0.6K0.4Fe2As2
• Transport and anisotropy in single-crystalline SrFe${}_2$As${}_2$ and $A_{0.6}$K${}_{0.4}$Fe${}_2$As${}_2$ ($A$ = Sr, Ba) superconductors
• Pressure-induced superconductivity in single crystal CaFe2As2
• Neutron diffraction on antiferromagnetic ordering in single-crystal BaFe2As2
• Pressure-induced superconductivity in Iron pnictide compound SrFe2As2
• Anisotropy of superconducting single crystal SmFeAsO_(0.8)F_(0.2) studied by torque magnetometry
• Evidence for two distinct anisotropies in the oxypnictide superconductors SmFeAsO_(0.8)F_(0.2) and NdFeAsO_(0.8)F_(0.2)