Superconductivity without Fe or Ni in the phosphides BaIr2P2 and BaRh2P2

Abstract

Heat capacity, resistivity, and magnetic susceptibility measurements confirm bulk superconductivity in single crystals of BaIr${}_2$P${}_2$ (T${}_c$=2.1K) and BaRh${}_2$P${}_2$ (T${}_c$ = 1.0 K). These compounds form in the ThCr${}_2$Si${}_2$ (122) structure so they are isostructural to both the Ni and Fe pnictides but not isoelectronic to either of them. This illustrates the importance of structure for the occurrence of superconductivity in the 122 pnictides. Additionally, a comparison between these and other ternary phosphide superconductors suggests that the lack of interlayer $P-P$ bonding favors superconductivity. These stoichiometric and ambient pressure superconductors offer an ideal playground to investigate the role of structure for the mechanism of superconductivity in the absence of magnetism.

Published in Phys Rev B: Rapid Communications

References in corpus (9)

• Superconductivity at 38 K in the iron arsenide (Ba1-xKx)Fe2As2
• Superconductivity up to 37 K in (A1-xSrx)Fe2As2 with A=K and Cs
• Superconductivity up to 29 K in SrFe2As2 and BaFe2As2 at high pressures
• Pressure-induced volume-collapsed tetragonal phase of CaFe2As2 as seen via neutron scattering
• The Unprecedented Giant Coupling of Fe-spin State and the As-As Hybridization in Iron-Pnictide
• Unconventional London penetration depth in Ba(Fe0.93Co0.07)2As2 single crystals
• Nickel-based phosphide superconductor with infinite-layer structure, BaNi2P2
• Superconductivity and the Effects of Pressure and Structure in Single Crystalline SrNi${}_2$P${}_2$
• Fermi surface in BaNi${}_2$P${}_2$