From thermally activated to viscosity controlled fracture of biopolymer hydrogels
arXiv:0810.4082 · doi:10.1063/1.3078267
Abstract
We report on rate-dependent fracture energy measurements over three decades of steady crack velocities in alginate and gelatin hydrogels. We evidence that, irrespective of gel thermo-reversibility, thermally activated "unzipping" of the non-covalent cross-link zones results in slow crack propagation, prevaling against the toughening effect of viscous solvent drag during chain pull-out, which becomes efficient above a few mm.s. We extend a previous model [Baumberger {\it et al.} Nature Materials, {\bf 5}, 552 (2006)] to account for both mechanisms, and estimate the microscopic unzipping rates.