Near-Zero Moment Ferromagnetism in the Semiconductor SmN

Abstract

The magnetic behaviour of SmN has been investigated in stoichiometric polycrystalline films. All samples show ferromagnetic order with Curie temperature (T_c) of 27 +/- 3 K, evidenced by the occurrence of hysteresis below T_c. The ferromagnetic state is characterised by a very small moment and a large coercive field, exceeding even the maximum applied field of 6 T below about 15 K. The residual magnetisation at 2 K, measured after cooling in the maximum field, is 0.035 mu_B per Sm. Such a remarkably small moment results from a near cancellation of the spin and orbital contributions for Sm3+ in SmN. Coupling to an applied field is therefore weak, explaining the huge coercive field . The susceptibility in the paramagnetic phase shows temperature-independent Van Vleck and Curie-Weiss contributions. The Van Vleck contribution is in quantitative agreement with the field-induced admixture of the J=7/2 excited state and the 5/2 ground state. The Curie-Weiss contribution returns a Curie temperature that agrees with the onset of ferromagnetic hysteresis, and a conventional paramagnetic moment with an effective moment of 0.4 mu_B per Sm ion, in agreement with expectations for the crystal-field modified effective moment on the Sm3+ ions.

5 pages, 3 figures

References in corpus (2)

• Ferromagnetic redshift of the optical gap in GdN
• Comparison between experiment and calculated band structures for DyN and SmN

Cited by in corpus (14)

• Rare-earth mononitrides
• Spin/orbit moment imbalance in the near-zero moment ferromagnetic semiconductor SmN
• Europium nitride: A novel diluted magnetic semiconductor
• Superconductivity in the ferromagnetic semiconductor SmN
• On the ferromagnetic ground state of SmN
• Twisted phase of the orbital-dominant ferromagnet SmN in a GdN/SmN heterostructure
• Electronic structure of rare-earth mononitrides: quasiatomic excitations and semiconducting bands
• Optical Spectroscopy of SmN: Evidence for 4f Transport
• Magnetism and electronic structure calculation of SmN
• 4f Conduction in the Magnetic Semiconductor NdN
• Tuneable magnetic behaviour, electronic structure and nitrogen vacancy formation in Gd${}_x$Sm${}_{1-x}$N
• Following enhanced Sm spin projection in Gd${}_x$Sm${}_{1-x}$N
• Magnetic transition in the $J_{\text{eff}}=1/2$ Kagomé system Sm${}_3$Sb${}_3$Zn${}_2$O${}_{14}$
• Epitaxial integration of the intrinsic ferromagnetic semiconductor GdN with silicon technology